Water-resistant polymer cement waterproof performance synthetic
pulp is imported acrylic emulsion polymer and inorganic powder
formulated in accordance with the proportion of science and have
some kind of two-component flexible waterproofing slurry. Has
excellent impermeability, waterproof, adhesive properties.
Technical indicators in line with JC / T 2090-2011 "polymer cement
waterproof slurry" requirement.
Aqueous slurry, non-toxic, harmless, energy saving, environmental
Strength, strong adhesion, water impermeability, good weather
In the wet surface of the base construction, short curing time,
which can effectively shorten the construction period;
Particularly suitable for the waterproof layer of decorative
materials (such as putty, plaster, tile, etc.) construction
Products barrel after opening the two-component Stir in proportion
to use, easy to operate, quick construction.
The perfect combination of two-component, acid, alkali, salt, mold,
stability can maintain a permanent waterproof;
Dosage: every millimeter thick film coating using about: 2.0Kg / m.
Suitable for toilet and bathroom, kitchen, ground floor, balconies,
terraces and other works of waterproof, impervious and moisture.
Handle all types of buildings seepage, leakage repair, all kinds of
pond water, seepage, etc.
All kinds of rigid surface seepage, waterproofing, sealing,
moisture and so on.
Primary treatment: Requires a solid, flat, smooth, not from the
sand, and have shed from the skin, loose animals and other
phenomena; cellular base surface, holes, cracks and down pipes and
other first with the plugging material around the block smooth,
sharp edges and protrusions should be removed, yin and yang angle
arc made of nodes; before brushing, spraying water mist application
base sufficiently moist (but not in water).
Paint preparation: First, slowly pour the powder supporting the
emulsion side down while stirring with an electric mixer, stir for
about 5 minutes until a homogeneous slurry, the slurry was allowed
to stand 10 minutes stirring after 2 minutes to fully matured.
Note: when secondary mixing stirrer at the bottom of the container,
do not do to enhance the sport, so as not to paste wrapped into the
air after a good tune slurry used within one hour.
Additional detailed structure waterproof coating layer: The yin and
yang angle, tube roots detailed structure should be additional
waterproof layer construction; For additional coating matrix
material should be caught in the middle, paving flat, no hollowing,
Alice, etc. , and is guaranteed to be completely soaked paint;
Waterproof coating layer construction: Scratch or brush can be
used, should be completed in 2 to 3 times; at points over the
coating, brushing should be on the next pass over the cured coating
dry before proceeding to the table after brushing twice direction
should be perpendicular to each other; when facade construction,
should be thin coating many times.
Should ensure a well-ventilated spot, suitable for the construction
of the ambient temperature 5 ~ 35 ℃, avoid exposure during the
Do other types of jobs in the construction area of the cross, after
the completion of the coating should be protected.
Paint should be used with the mix with, and should be used within a
specified time, usually after mixing paint not more than one hour,
in order to avoid waste.
Sprinkler maintenance should be performed two to three days after
construction ends 24 hours.
Water testing and paste tiles should, after 72 hours drying and
curing the coating. Lower temperatures should be extended. For
pasting tiles on waterproof coating, we recommend using a dedicated
low-grade cement tile adhesive or mortar paste.
Storage and transport
This product is flame retardant materials, according to general
cargo transport. Transport should avoid the rain, sunlight, cold,
prohibit the collision, extrusion, and keep the packaging intact.
The product should be in a dry, ventilated, cool place storage,
storage temperature should not fall below 5 ℃.
Under normal transportation, storage conditions, from the date of
production of the storage period of not less than 12 months.